Ferric chloride evaporation and crystallization equipment is required. The original technical approach was too costly, requiring an efficient evaporator. However, ferric chloride is too corrosive, making it difficult to choose suitable materials; it would be great if there were good solutions or equipment available
It’s too expensive; I’m not sure if using F4 will work
Material F4 is corrosion-resistant but has poor thermal conductivity; graphite and enamel can be considered as alternatives~~
I don’t know what C-276 is. Zirconium materials are truly expensive; as for graphite, it’s unclear what its strength is – perhaps the purity of the product is difficult to control. If the temperature shock is not severe, using enamel might be a good option.
C-276 is a type of Hastelloy