Discussing hydrogen corrosion and protection measures

Thread Content

1. Hydrogen bubbling: In low-strength steels, especially those containing a large amount of non-metallic inclusions, the hydrogen atoms generated in the solution can easily diffuse into the metal. Most of this hydrogen combines to form H2 and escapes through the wall of the container, but a small amount remains trapped in the voids within the steel, where it also combines to form H2. Since hydrogen molecules cannot diffuse, this accumulation leads to high internal pressures, causing bubbles to form on the surface of the steel, or even causing it to crack. 　　When the environment contains toxins such as sulfides, cyanides, and phosphorus-containing ions that prevent the hydrogen release reaction, hydrogen atoms enter the steel and cause bubbling. Materials in the petroleum industry often contain the aforementioned elements, and hydrogen bubbling is a common hazard. Prevention method: Removing such elements is the most effective approach ； Hole-free calm steel can also be used as a substitute for boiling steel, which contains numerous holes. In addition, linings made of austenitic stainless steel or nickel, which are resistant to hydrogen penetration, or rubber, plastic, ceramic tiles, along with the use of corrosion inhibitors, can be employed. 2. Hydrogen embrittlement: In high-strength steels, the lattice undergoes significant deformation; when hydrogen enters, the lattice structure changes further, resulting in a decrease in toughness and ductility and thus embrittlement, which can lead to fracture under external forces. However, before rupture, hydrogen embrittlement is reversible; by undergoing appropriate heat treatment to allow hydrogen to escape, the metal can regain its original properties. Generally, the higher the strength of steel, the greater its susceptibility to hydrogen embrittlement fracture. Its mechanism is not yet fully understood; there are various theories, such as: the accumulation of hydrogen molecules creating high internal pressure ； The adsorption of hydrogen reduces the surface energy, or affects the bond strength of atomic bonds, thereby promoting dislocation motion. Some indications suggest that ferritic and martensitic ferroalloys react with hydrogen at the crack tips, while metals such as titanium and tantalum, which readily form hydrides, tend to react with dissolved hydrogen at high temperatures to produce brittle hydrides. Hydrogen can also cause decarburization at high temperatures. 　　Hydrogen that enters metals is often generated in operations such as electroplating, welding, pickling, and cathodic protection. After the crack tip is acidified due to stress corrosion, hydrogen embrittlement also occurs, but anodic corrosion has caused permanent damage, which is different from simple hydrogen embrittlement. Hydrogen embrittlement is not related to voids in steel; therefore, the prevention methods differ slightly from those for preventing hydrogen blistering: in environments where hydrogen embrittlement is likely to occur, it is advisable to avoid using high-strength steels, and Ni or Cr alloyed steels can be used instead ； Use low-hydrogen welding electrodes during welding, and keep the environment dry (water is the main source of hydrogen) ； The plating solution needs to be selected, and the current must be controlled ； A corrosion inhibitor is added to the pickling solution. After hydrogen has entered the metal, low-temperature baking can be used to remove it; for steel, dehydration generally takes place at 90–150°C.