CO H2 CO2 N2 CH4 H2S COS AR H2O H3N 0.448195 0.357470 0.185299 0.003117 0.000496 0.001412 7.01E-05 0.001536 0.002346 5.93E-05 In the denitrification system, the composition of the feed gas is as above; could someone please offer some advice? What material should be used for the selection of the inner components? Will 304 work?

Reply #22009-03-01

The 304 material should not present any major issues; having an extra 2 millimeters of corrosion margin will ensure no problems even after 20 years of use

Reply #32009-03-04

If it is increased by another 2mm, can the device operate for 20 years? It seems a bit of a waste

Submit a Project

**Looking for Chemical Technology, Equipment & Solutions?** No Registration Required Broader Platform Exposure | Global Chemical Service Provider Connections

Submit Request — Free Consultation

Disclaimer

This is an automated machine translation of the original thread. Some technical terms may have inaccuracies; the original text shall prevail. Click "View Original" at the top right to access the source page, which supports IP-based automatic real-time language translation. Please watch out for contact details and sales inducements to prevent fraud. All content and translations are for reference only, representing solely the poster's personal views. For enquiries, email service@hcbbs.com.

Transformation unit: Selection of deamination materials

Thread Content

Related Threads in This Forum

← Previous

Next →

Submit a Project

Disclaimer

Quick Links