2009-03-10View Original

Thread Content

What welding material should be used for surfacing on Q235 to obtain 1Cr13? What kind of process is required, and what thickness should the surfacing layer have? Thank you

Reply #22009-03-10

Refer to Appendix A of JB/T4709-2000; pay attention to the welding temperature and post-weld heat treatment: A402 3mm + A302 3mm

Submit a Project

**Looking for Chemical Technology, Equipment & Solutions?** No Registration Required Broader Platform Exposure | Global Chemical Service Provider Connections

Submit Request — Free Consultation

Disclaimer

This is an automated machine translation of the original thread. Some technical terms may have inaccuracies; the original text shall prevail. Click "View Original" at the top right to access the source page, which supports IP-based automatic real-time language translation. Please watch out for contact details and sales inducements to prevent fraud. All content and translations are for reference only, representing solely the poster's personal views. For enquiries, email service@hcbbs.com.

What welding material should be cladded on Q235 to ultimately obtain 1Cr13?

Thread Content

Related Threads in This Forum

← Previous

Next →

Submit a Project

Disclaimer

Quick Links