What is the appropriate hardness range for babbitt alloy?

2010-09-14View Original

Thread Content

What is the appropriate hardness range for babbitt alloy?

Reply #22010-09-17

Material Typical plate ASTM B575 Yield strength (0.2% strain) 345 MPa 310* MPa Tensile strength 724 MPa 690* MPa Elongation % (51 mm) 67% 45% Hardness 87 HRB 100** HRB* Minimum **Maximum

Reply #32011-11-10

Tin antimony: ZChSnSb11-6, HB>27; ZChSnSb4-4, HB>20; ZChSnSb8-4, HB>24; Lead antimony: ZChPbSb16-16-2, HB>30; ZChPbSb15-5-3, HB>32

Submit a Project

**Looking for Chemical Technology, Equipment & Solutions?** No Registration Required Broader Platform Exposure | Global Chemical Service Provider Connections

Submit Request — Free Consultation

Disclaimer

This is an automated machine translation of the original thread. Some technical terms may have inaccuracies; the original text shall prevail. Click "View Original" at the top right to access the source page, which supports IP-based automatic real-time language translation. Please watch out for contact details and sales inducements to prevent fraud. All content and translations are for reference only, representing solely the poster's personal views. For enquiries, email service@hcbbs.com.

Quick Links