SMAW flux issues
Thread Content
During flaw detection, why does the submerged arc welding flux end up in the weld? Could anyone with expertise give some guidance? Thank you
The flux just fell back in again. Could it be that the flux isn’t clean enough?
It’s probably not flux; it’s some other debris that hasn’t melted
What you’re describing is impossible; it should be slag inclusions.