I would like to ask fellow sailors: for a mixture containing n-octanol and trioctylamine, what material is suitable? Excluding steel products.
Besides steel, PE-lined steel can be considered; it will not suffer from corrosion or swelling.
Steel-reinforced plastic composite pipes can be considered, but the temperature must not be too high; it should not exceed 80 degrees.
Temperature? Pressure? -----------
It’s non-metallic! But temperature does matter! Better PTFE has a higher temperature resistance!
Temperature, pressure? Fiberglass material can be considered: http://www.mxsgl.com
It depends on the operating temperature: if it’s below 80 degrees, PE can be considered; if it’s above 80 degrees, PTFE or F40 is a better choice. You can contact me at QQ635098707
It can be lined with PO or lead plating. Lining with PO is not very costly, but it cannot withstand high temperatures; lead plating is more expensive, yet it provides excellent results