12cr1movGの接管とQ345R製シェルを溶接した後、溶接後の熱処理温度はどのように決めるべきか？
異種鋼材の溶接後の熱処理温度は、溶接後熱処理温度が高い方の鋼種に準じて行うが、その温度は両鋼種のうちいずれか一方の下限臨界点Ac1を超えてはならない。
**Looking for Chemical Technology, Equipment & Solutions?** No Registration Required Broader Platform Exposure | Global Chemical Service Provider Connections
Submit Request — Free ConsultationThis is an automated machine translation of the original thread. Some technical terms may have inaccuracies; the original text shall prevail. Click "View Original" at the top right to access the source page, which supports IP-based automatic real-time language translation. Please watch out for contact details and sales inducements to prevent fraud. All content and translations are for reference only, representing solely the poster's personal views. For enquiries, email service@hcbbs.com.