Can high-temperature steam pipes be reused?
Thread Content
Can high-temperature steam pipes be reused? There are two identical field units; can the high-temperature steam pipeline used for testing be reused with these two units? If it’s possible, then what are the things to keep in mind? Thank you
Do you plan to move it from one place to another? This is possible, but why do we need to do this?
It can be reused; once cut, it can be transferred to a new device and welded back together. It was used for testing, and hasn’t been in use for long.
It is necessary to ensure that all documents are complete, and it is advisable to have the new pipeline inspected by a specialized inspection agency before installation.
At present, as long as there is no severe rusting, there should be no problem