Can 304 steel be used with 30% sulfuric acid at 30-40°C? ? ?
Thread Content
Can 304 steel be used with 30% sulfuric acid at 30-40°C? ? ?
At your specified concentration and temperature, it is not recommended to use 304 material; according to the corrosion curve, the annual corrosion rate is nearly 3 mm. It is recommended to move it to the Mechanical-Corrosion section; a master will reply to your question
May I upload the corrosion curve? ? ?
I just took a photo of it with my phone, but it wasn’t uploaded; I’ll take a screenshot on the computer for you
Is this corrosion curve the one from up there? I’d like to look up some information; could you upload it? Thank you very much
Thank you for sharing. Where is it from?
It’s a reference book; I just saw the post comments. I’ll get back to you or upload the reference book file when I have time
The name is a bit long; I forgot it. I don’t have it on my phone; I’ll reply once I’m online on the computer
The screenshot is from page P203 of \"Corrosion and Protection of Process Equipment (2nd Edition), 2009\". Since the file is a bit large, it has been divided into 3 compressed files. I need to download it myself, right?