Inconel 600’s resistance to salt and acid corrosion
Thread Content
I would like to ask everyone: at room temperature and normal pressure, what is the maximum concentration of saline acid that Inconel 600 can withstand in terms of corrosion resistance? Thank you all! ! !
Not suitable for use in hydrochloric acid environments, as it is prone to pitting
Is it a pipeline or equipment? What device? For acids at normal temperature and pressure, it is recommended to use non-metallic materials. Such as PP, PVC, PE, etc.; in cases where there is certain pressure or high temperatures, it is recommended to use impermeable graphite.
Not recommended due to severe corrosion.
This material is not only expensive, but also difficult to maintain! This material is practically useless against chloride ions; it should be noted that corrosion occurs at lower temperatures even faster than in carbon steel!