I would like to ask the experts here! The problem of asphalt blending.
Thread Content
I would like to ask the experts here! When producing direct-current asphalt from mixed heavy oil, if the penetration value, softening point, or ductility do not meet the required standards, how can these issues be addressed? Is it possible to reprocess the material? Thank you all! ! !
It is possible; it can be blended using residue oil or aromatic oil with different penetration values
Question! If the softening point and ductility of that asphalt do not meet the requirements, can it still be blended?
Ductility can be adjusted using our SBR; Tahe and Changqing are both using it
You need to see exactly what causes the non-compliance; if the asphalt is too heavy, the blending process can be simplified