Modifications to glass-lined reaction vessels
Thread Content
https://bbs.hcbbs.com/forum.php?mod=image&aid=1777362&size=300x300&key=8b260b9b66083cde&nocache=yes&type=fixnone https://bbs.hcbbs.com/forum.php?mod=image&aid=1777363&size=300x300&key=69722298337d6326&nocache=yes&type=fixnone During the installation of the new project, the holes in the steel structure were too small; the installer suggested cutting out those parts and welding them back in. I’m worried that this might cause magnetic explosion. And also, why must lifting be done from bottom to top, rather than from top to bottom?
Generally, this does not happen, as there is a jacket – that is, there is an air layer of about 5 centimeters between the outer layer and the inner layer. As for lifting, there is no rule stating that it must be done from bottom to top.
What level of flatness can glass-lined surfaces achieve, and how thick can the coating be applied? Please provide some information