Thread Content

The thickness of the pqr welding specimen is 7.11; why is the thickness range for the base material specified in the WPS as 3.555–13.11? According to ASME IX

Reply #22020-12-25

The evaluated thickness ranges from 0.5 to 1.5 times the thickness of the specimen

Reply #32020-12-26

What’s the problem? ? What was said upstairs is one of those situations. . . . .

Reply #42020-12-26

The title is ASME Volume IX, while the content is NB/T47014

Reply #52020-12-26

There are several cases: for specimens that have not been heat-treated and those that have been heat-treated, the coating thickness varies even when the thickness of the specimens is the same. This is explained in detail in the relevant standard specifications; I remember there is a comparison table for this

Submit a Project

**Looking for Chemical Technology, Equipment & Solutions?** No Registration Required Broader Platform Exposure | Global Chemical Service Provider Connections

Submit Request — Free Consultation

Disclaimer

This is an automated machine translation of the original thread. Some technical terms may have inaccuracies; the original text shall prevail. Click "View Original" at the top right to access the source page, which supports IP-based automatic real-time language translation. Please watch out for contact details and sales inducements to prevent fraud. All content and translations are for reference only, representing solely the poster's personal views. For enquiries, email service@hcbbs.com.

ASME IX welding thickness coverage – assistance needed

Thread Content

Related Threads in This Forum

← Previous

Next →

Submit a Project

Disclaimer

Quick Links