Materials for high-temperature and high-pressure reactors
Thread Content
The design process temperature is around 200 degrees, with a pressure of 15 MPa; alkali and chloride ions are generated during this process. What type of material would be suitable for use in the reactor?
What is the chloride ion concentration? How high is the alkali concentration? It seems that pure nickel composite sheets or nickel-based alloy composite sheets are suitable
If I use this, what software should I use for the calculations?
Hello, as a newcomer to this field, do you have any calculation tables and materials related to high-temperature and high-pressure reactors? If you have any, could you share them?
For small reaction vessels, Hastelloy is sufficient. For large equipment, composite panels are used.