I would like to ask about the corrosion resistance of the following materials to high-temperature concentrated sulfuric acid

2021-02-20View Original

Thread Content

I would like to ask for your expertise: what is the corrosion resistance of the materials N08020, N08926, and C-276 in concentrated sulfuric acid at a temperature of around 180°C? Are there any practical application cases, and what are the results?

Reply #22021-02-22

I have some information related to these several grades

Reply #32021-02-25

C276 can only be used at temperatures not too high in sulfuric acid, below 100°C

Reply #42021-02-25

Could you provide it? Thank you, email: 5488646@qq.com

Reply #52021-03-24

They are all nickel-based stainless steels; they shut off completely at 180 degrees and cannot be used

Submit a Project

**Looking for Chemical Technology, Equipment & Solutions?** No Registration Required Broader Platform Exposure | Global Chemical Service Provider Connections

Submit Request — Free Consultation

Disclaimer

This is an automated machine translation of the original thread. Some technical terms may have inaccuracies; the original text shall prevail. Click "View Original" at the top right to access the source page, which supports IP-based automatic real-time language translation. Please watch out for contact details and sales inducements to prevent fraud. All content and translations are for reference only, representing solely the poster's personal views. For enquiries, email service@hcbbs.com.

I would like to ask about the corrosion resistance of the following materials to high-temperature concentrated sulfuric acid

Thread Content

Related Threads in This Forum

← Previous

Next →

Submit a Project

Disclaimer

Quick Links