Titanium-steel composite equipment
Thread Content
For the pipe ends of titanium-steel composite equipment, the inner layer is made of titanium tube, with a steel tube surrounding it on the outside; there is a 1 mm gap between the titanium tube and the steel tube. If an additional jacket is installed around the outer steel tube to provide heat insulation for the pipe end, will this jacket have any impact on such pipe ends, and could it cause deformation?
A 1MM gap can be seen in the titanium-steel composite pipe! Which company manufactured it? Could you send a photo to confirm? It’s hard to imagine what it will look like. Titanium-steel composites are generally produced by explosion or explosion-rolling; the presence of gaps indicates that the product is defective. So why is the person in question still considering whether an insulation jacket might cause deformation at the pipe end? As long as it is a qualified product, the temperature of the insulation jacket generally won’t be too high, and it certainly won’t cause deformation at the pipe ends ； However, if there is a gap, the titanium tube with a very thin wall thickness is deformed by the pressure inside the tube, rather than being deformed by the insulation jacket.
The cylinder is manufactured by explosive lamination; the device’s ports consist of steel tubes enclosed within titanium tubes, and 290-grade heat transfer oil is used for heating inside the jacket. I’m not sure how significant this will be
Steel pipes can also be used for explosive lamination – could you send a photo? I really want to see that 1MM gap! 290 degrees does not have an adverse effect on titanium materials; do not exceed 300 degrees.
Hello, are you from a equipment manufacturing company? Let’s exchange ideas
No, I’m also a user, hehe
It won’t have any impact. We are currently developing this steel-titanium composite device, which also features internal coiled tubes for heating.
Hello, are your containers vertical or horizontal? Are you a equipment manufacturer? Let’s exchange some ideas
What the manufacturing plant produces are vertical reaction vessels
Which company manufactured your reaction kettle?
Titanium-steel composite plates can withstand 290° thermal oil; if there are gaps or defects, then it is definitely an inferior product. These composite plates can be bonded together easily during welding, and they also exhibit excellent corrosion resistance even in the presence of highly corrosive substances；