Is the corrosive effect of chloride ions on stainless steel very weak under alkaline conditions? Thank you
Thread Content
Can 304 steel withstand a 4% sodium chloride solution at PH10-12? Is the corrosive effect of chloride ions on stainless steel very weak under alkaline conditions? Thank you
Chloride ions in an alkaline environment accelerate the corrosion of stainless steel even more! Especially in terms of crystal corrosion, it is recommended to use 2205 duplex stainless steel; at the very least, 316L stainless steel should be used! If using Tai material is possible, don’t worry!
If the temperature is not high, plastic material will suffice
What was said upstairs is correct – chloride ions in an alkaline environment cause greater corrosion of stainless steel! Especially for crystal corrosion, it is recommended to use 2205 duplex stainless steel; if you need a sample of 2205 duplex steel, please contact me
We can provide hanging slab experiments