Is 2205 duplex stainless steel resistant to chloroacetic acid corrosion?
Thread Content
The company is planning to install a chloroacetic acid unpacking machine – can material 2205 withstand corrosion? Please ask an expert to help answer
Solid chloroacetic acid? Is 316L not good? Just go straight to 2205; you have the money
It is solid chloroacetic acid; there is concern that the hydrolysis of chloroacetic acid could cause corrosion
Is the unpacking machine you made designed for unpacking ton bags? Indeed, chloroacetic acid can cause corrosion, but it should not be a problem with the reaction equipment. PS: Liquid chloroacetic acid can also be handled using 316L pipes
Is it the breakdown of ton bags? Is the corrosion caused by hydrolyzed chloroacetic acid due to chloride ions or hydrochloric acid? Are there any reference documents? Thank you!
Chloroacetic acid, also known as monochloroacetic acid, has the formula Cl-CH2-COOH; it is the -COOH group that causes corrosion, and there is no hydrochloric acid or chloride ions involved.
Hello, I was wondering if a packaging-unpacking machine has been ordered. Where was it ordered? I would like to order one as well for unpacking chloroacetic acid