Let's take a look at whether there are any problems with the processing technology of steel-lined graphite towers?

2022-04-08View Original

Thread Content

Let's take a look at whether there are any problems with the processing technology of steel-lined graphite towers? Medium: 15% hydrochloric acid, 40% sulfuric acid, carbon disulfide, low pressure steam. Pressure 0.3-0.4MPa, temperature 0-150 degrees

Reply #22022-04-08

This post was last edited by Shutong on 2022-4-8 18:56. Please check against the following standards HGT 2370-2017 Technical conditions for chemical equipment made of impermeable graphite HGT 5631-2019 Evaluation of bonding process of impermeable graphite equipment GBT 35926-2018 Technical specifications for bonding operations of impermeable graphite GBT 35922-2018 Technical Specifications for Corrosion Resistance Operations of Impermeable Graphite Impregnation

Submit a Project

**Looking for Chemical Technology, Equipment & Solutions?** No Registration Required Broader Platform Exposure | Global Chemical Service Provider Connections

Submit Request — Free Consultation

Disclaimer

This is an automated machine translation of the original thread. Some technical terms may have inaccuracies; the original text shall prevail. Click "View Original" at the top right to access the source page, which supports IP-based automatic real-time language translation. Please watch out for contact details and sales inducements to prevent fraud. All content and translations are for reference only, representing solely the poster's personal views. For enquiries, email service@hcbbs.com.

Let's take a look at whether there are any problems with the processing technology of steel-lined graphite towers?

Thread Content

Related Threads in This Forum

← Previous

Next →

Submit a Project

Disclaimer

Quick Links