NACE treatment, liquid-contacting part
Thread Content
As the title suggests, what does this mean? The product is a magnetic flap level gauge, and the medium used is rich amine liquid. Design book material: 316SS. It is a 316SS pipe. Lining F4?
NACE are the standards related to surface treatment issued by the American Society of Corrosion Engineers.
In media containing humid hydrogen sulfide, the materials used in the parts of instruments that come into contact with such media must be treated according to NACE standards, as H2S is stress-sensitive and causes stress corrosion; therefore, the hardness of metal materials needs to be reduced in order to resist H2S-induced corrosion. NACE treatment is generally heat treatment.
NACE is a corrosion protection method, not an issue with the lining.
Partial list of NACE (National Association of Corrosion Engineers) standards:
01 NACE MR 0174 – Recommended method for screening corrosion inhibitors for piston rod lubricants
02 NACE MR 0175 – Metallic materials resistant to sulfide stress cracking in oilfield equipment
03 NACE MR 0176 – Metallic materials for piston pumps used in corrosive oilfield environments
04 NACE MR 0274 – Technical specifications for cold-wrap tape materials used in coatings for underground or underwater pipelines
05 NACE No.1 – Standard for overall surface preparation resulting in a silver-white finish after metal blasting
06 NACE No.2 – Standard for overall surface preparation resulting in a silver-white finish after metal blasting
07 NACE No.3 – Standard for overall surface preparation via commercial sandblasting
08 NACE No.4 – Standard for surface preparation by wire brushing to remove rust
09 NACE No.5 – High-pressure and ultra-high-pressure water jet treatment and cleaning of steel and other hard materials prior to recoating
10 NACE RP 0169 – External corrosion control for underground or underwater pipeline systems
11 NACE RP 0170 – Protection against polythionic acid stress corrosion cracking on austenitic stainless steels and other austenitic alloys during refinery shutdowns
12 NACE RP 0176 – Corrosion control for steel fasteners on offshore platforms in petroleum production
13 NACE RP 0177 – Methods to mitigate the effects of alternating current and lightning on corrosion control devices on metal structures
14 NACE RP 0178 – Design, fabrication, and surface finishing of storage tanks and vessels intended for lining
15 NACE RP 0180 – Cathodic protection for wastewater treatment units in paper mills
16 NACE RP 0181 – Internal protective coatings for oilfield equipment containing liquids
17 NACE RP 0182 – Initial conditioning of cooling water equipment
18 NACE RP 0184 – Repair of lined systems
19 NACE RP 0185 – Protective layer made of extruded polypropylene resin with soft adhesive for use on underground or underwater pipelines
20 NACE RP 0186 – Cathodic protection for the external surfaces of steel casing in oil wells
21 NACE RP 0187 – Design considerations for controlling corrosion of steel reinforcement in concrete
22 NACE RP 0188 – Testing of defective areas in protective coatings
23 NACE RP 0189 – Online monitoring of cooling water
24 NACE RP 0190 – External protective coatings for joints, fittings, and valves in underground or underwater metal pipeline systems
25 NACE RP 0191 – Application of external plastic coatings to tubular oilfield equipment and accessories
26 NACE RP 0192 – Corrosion monitoring of steel components in oil and gas production
27 NACE RP 0193 – External cathodic protection for the bottoms of metal storage tanks
28 NACE RP 0194 – Standards and test methods for cathodic protection of lead-clad cables
29 NACE RP 0195 – Recommended practices for controlling corrosion of piston rods exposed to chemical media
30 NACE RP 0196 – Sacrificial anode protection for the interior surfaces of steel water storage tanks
31 NACE RP 0273 – Handling and application of corrosion inhibitors in oilfields
32 NACE RP 0274 – High-pressure testing of pipeline coatings prior to installation
33 NACE RP 0281 – Evaluation of atmospheric exposure test methods for coated specimens
34 NACE RP 0285 – Corrosion control via cathodic protection for underground storage tanks
35 NACE RP 0286 – Electrical insulation in cathodic protection management
36 NACE RP 0287 – Field measurement of surface profiles after steel blasting using replica tape
37 NACE RP 0288 – Inspection of lining layers on steel and concrete
38 NACE RP 0290 – Cathodic protection for steel reinforcement in concrete structures exposed to atmospheric conditions
39 NACE RP 0291 – Installation, operation, and management of internally plastic-coated tubular oilfield equipment and accessories
40 NACE RP 0292 – Installation of thin-walled metal linings in air pollution control and other process equipment
41 NACE RP 0294 – Design, fabrication, and inspection of storage tanks for storing concentrated sulfuric acid and fuming sulfuric acid at room temperature
42 NACE RP 0295 – Application of internal coating systems to new and existing rail tank cars
43 NACE RP 0296 – Guidelines for detecting, repairing, and protecting cracks in operating petroleum refining pressure vessels in humid environments
44 NACE RP 0375 – Paraffin-based protective coatings for underground pipeline systems
45 NACE RP 0376 – Integral organic corrosion-resistant flooring
46 NACE RP 0386 – Application of internal coating systems to rail tank cars transporting plastics, foodstuffs, and chemicals
47 NACE RP 0387 – Metallurgical and inspection requirements for cast sacrificial anodes used in offshore protection
48 NACE RP 0388 – Impressed current cathodic protection for interior surfaces of steel water tanks
49 NACE RP 0390 – Maintenance guidelines for corrosion control systems in existing reinforced concrete structures
50 NACE RP 0391 – Materials suitable for handling and storing concentrated H₂SO₄ (90%–100%) at room temperature
51 NACE RP 0392 – Restoration and re-passivation of open-loop cooling water systems following low-pH operation
52 NACE RP 0394 – Application, performance, and quality control of fusion-bonded epoxy coatings applied to exterior surfaces of pipelines constructed on-site
53 NACE RP 0395 – Epoxy-coated, steel-reinforced retaining walls
54 NACE RP 0472 – Methods to prevent environmental cracking of carbon steel welds in corrosive petroleum refining media
55 NACE RP 0475 – Selection of materials resistant to corrosion by various phases following addition of water treatment agents to oil-containing media
56 NACE RP 0487 – Selection and evaluation criteria for petroleum-based intermediate coatings
57 NACE RP 0490 – Detection of defects in fusion-bonded epoxy coatings on pipelines with defect sizes ranging from 250 to 760 micrometers (10–30 mils)
58 NACE RP 0491 – Checklist for selecting non-metallic welding systems for oilfield applications
59 NACE RP 0492 – Metallurgical parameters and inspection requirements for bracelet-type anodes used on submarine pipelines
60 NACE RP 0495 – Guidelines for improving the qualifications of personnel engaged in sandblasting, coating, and lining work in the railway industry
61 NACE RP 0572 – Design, installation, operation, and maintenance of deep-buried impressed current grounding beds
62 NACE RP 0575 – Internal cathodic protection systems for petroleum processing vessels
63 NACE RP 0590 – Recommended methods for detecting, protecting, and repairing cracks in air separators
64 NACE RP 0591 – Coatings for concrete surfaces exposed to non-submerged and atmospheric environments
65 NACE RP 0592 – Application of internal coating systems to new and existing rail tank cars transporting concentrated sulfuric acid (90%–98%)
66 NACE RP 0675 – Corrosion control for external surfaces of submarine steel pipes
67 NACE RP 0690 – Standard format for data collection and editing for input into databases of corrosion-resistant materials
68 NACE RP 0692 – Application of external coating systems to steel railway tank cars
69 NACE RP 0775 – Preparation, installation, and analysis of corrosion coupons in oilfield operations
70 NACE RP 0792 – Standard format for periodic computer-based data surveys
71 NACE RP 0892 – Linings for submerged concrete equipment surfaces
72 NACE TM 0169 – Laboratory corrosion testing of metals
73 NACE TM 0171 – Autoclave corrosion testing of metals in high-temperature water
74 NACE TM 0172 – Determination of corrosion behavior of various materials in petroleum production pipelines
75 NACE TM 0173 – Test method for evaluating the quality of subsurface injection water using membrane filters
76 NACE TM 0174 – Laboratory evaluation methods for protective coatings and lining materials used in equipment containing solutions
77 NACE TM 0177 – Laboratory test methods for metals exhibiting specific forms of cracking under H₂S-containing environments
78 NACE TM 0183 – Evaluation of internally plastic-coated tubular equipment for corrosion control in aqueous flowing media
79 NACE TM 0184 – Accelerated test methods for selecting atmospheric corrosion-resistant surface coatings for offshore platforms and equipment
80 NACE TM 0185 – Autoclave test evaluation of internally corrosion-resistant plastic coatings on tubular equipment
81 NACE TM 0186 – Detection of defects in internal pipe coatings with dry film thicknesses ranging from 250 to 760 micrometers (10–30 mils)
82 NACE TM 0187 – Evaluation of elastomeric materials in sour gas environments
83 NACE TM 0190 – Impressed current test method for laboratory testing of aluminum anodes
84 NACE TM 0192 – Evaluation of elastomeric materials in carbon dioxide compressor environments
85 NACE TM 0193 – Laboratory corrosion testing of metals in refined chemical cleaning solutions at temperatures below 93°C (200°F)
86 NACE TM 0194 – Field monitoring of bacterial growth in oilfield systems
87 NACE TM 0196 – Periodic evaluation of corrosion resistance of polymeric materials
88 NACE TM 0274 – Dynamic corrosion testing of metals in high-temperature water
89 NACE TM 0275 – Testing of steel and fiber-reinforced plastic piston performance using hybrid mixing and alternating rod methods
90 NACE TM 0284 – Evaluation of resistance to hydrogen-induced cracking in pipelines and pressure vessels
91 NACE TM 0286 – Cooling water test apparatus for heat transfer surfaces
92 NACE TM 0294 – Testing of embeddable anodes in atmospherically exposed reinforced concrete
93 NACE TM 0296 – Evaluation of elastomeric materials in acidic liquid environments
94 NACE TM 0374 – Laboratory screening tests for anti-scaling capabilities aimed at preventing calcium sulfate and calcium carbonate deposition
95 NACE TM 0384 – Defect detection in internal pipe coatings with dry film thicknesses less than 250 micrometers (10 mils)
01 NACE MR 0174 – Recommended method for screening corrosion inhibitors for piston rod lubricants
02 NACE MR 0175 – Metallic materials resistant to sulfide stress cracking in oilfield equipment
03 NACE MR 0176 – Metallic materials for piston pumps used in corrosive oilfield environments
04 NACE MR 0274 – Technical specifications for cold-wrap tape materials used in coatings for underground or underwater pipelines
05 NACE No.1 – Standard for overall surface preparation resulting in a silver-white finish after metal blasting
06 NACE No.2 – Standard for overall surface preparation resulting in a silver-white finish after metal blasting
07 NACE No.3 – Standard for overall surface preparation via commercial sandblasting
08 NACE No.4 – Standard for surface preparation by wire brushing to remove rust
09 NACE No.5 – High-pressure and ultra-high-pressure water jet treatment and cleaning of steel and other hard materials prior to recoating
10 NACE RP 0169 – External corrosion control for underground or underwater pipeline systems
11 NACE RP 0170 – Protection against polythionic acid stress corrosion cracking on austenitic stainless steels and other austenitic alloys during refinery shutdowns
12 NACE RP 0176 – Corrosion control for steel fasteners on offshore platforms in petroleum production
13 NACE RP 0177 – Methods to mitigate the effects of alternating current and lightning on corrosion control devices on metal structures
14 NACE RP 0178 – Design, fabrication, and surface finishing of storage tanks and vessels intended for lining
15 NACE RP 0180 – Cathodic protection for wastewater treatment units in paper mills
16 NACE RP 0181 – Internal protective coatings for oilfield equipment containing liquids
17 NACE RP 0182 – Initial conditioning of cooling water equipment
18 NACE RP 0184 – Repair of lined systems
19 NACE RP 0185 – Protective layer made of extruded polypropylene resin with soft adhesive for use on underground or underwater pipelines
20 NACE RP 0186 – Cathodic protection for the external surfaces of steel casing in oil wells
21 NACE RP 0187 – Design considerations for controlling corrosion of steel reinforcement in concrete
22 NACE RP 0188 – Testing of defective areas in protective coatings
23 NACE RP 0189 – Online monitoring of cooling water
24 NACE RP 0190 – External protective coatings for joints, fittings, and valves in underground or underwater metal pipeline systems
25 NACE RP 0191 – Application of external plastic coatings to tubular oilfield equipment and accessories
26 NACE RP 0192 – Corrosion monitoring of steel components in oil and gas production
27 NACE RP 0193 – External cathodic protection for the bottoms of metal storage tanks
28 NACE RP 0194 – Standards and test methods for cathodic protection of lead-clad cables
29 NACE RP 0195 – Recommended practices for controlling corrosion of piston rods exposed to chemical media
30 NACE RP 0196 – Sacrificial anode protection for the interior surfaces of steel water storage tanks
31 NACE RP 0273 – Handling and application of corrosion inhibitors in oilfields
32 NACE RP 0274 – High-pressure testing of pipeline coatings prior to installation
33 NACE RP 0281 – Evaluation of atmospheric exposure test methods for coated specimens
34 NACE RP 0285 – Corrosion control via cathodic protection for underground storage tanks
35 NACE RP 0286 – Electrical insulation in cathodic protection management
36 NACE RP 0287 – Field measurement of surface profiles after steel blasting using replica tape
37 NACE RP 0288 – Inspection of lining layers on steel and concrete
38 NACE RP 0290 – Cathodic protection for steel reinforcement in concrete structures exposed to atmospheric conditions
39 NACE RP 0291 – Installation, operation, and management of internally plastic-coated tubular oilfield equipment and accessories
40 NACE RP 0292 – Installation of thin-walled metal linings in air pollution control and other process equipment
41 NACE RP 0294 – Design, fabrication, and inspection of storage tanks for storing concentrated sulfuric acid and fuming sulfuric acid at room temperature
42 NACE RP 0295 – Application of internal coating systems to new and existing rail tank cars
43 NACE RP 0296 – Guidelines for detecting, repairing, and protecting cracks in operating petroleum refining pressure vessels in humid environments
44 NACE RP 0375 – Paraffin-based protective coatings for underground pipeline systems
45 NACE RP 0376 – Integral organic corrosion-resistant flooring
46 NACE RP 0386 – Application of internal coating systems to rail tank cars transporting plastics, foodstuffs, and chemicals
47 NACE RP 0387 – Metallurgical and inspection requirements for cast sacrificial anodes used in offshore protection
48 NACE RP 0388 – Impressed current cathodic protection for interior surfaces of steel water tanks
49 NACE RP 0390 – Maintenance guidelines for corrosion control systems in existing reinforced concrete structures
50 NACE RP 0391 – Materials suitable for handling and storing concentrated H₂SO₄ (90%–100%) at room temperature
51 NACE RP 0392 – Restoration and re-passivation of open-loop cooling water systems following low-pH operation
52 NACE RP 0394 – Application, performance, and quality control of fusion-bonded epoxy coatings applied to exterior surfaces of pipelines constructed on-site
53 NACE RP 0395 – Epoxy-coated, steel-reinforced retaining walls
54 NACE RP 0472 – Methods to prevent environmental cracking of carbon steel welds in corrosive petroleum refining media
55 NACE RP 0475 – Selection of materials resistant to corrosion by various phases following addition of water treatment agents to oil-containing media
56 NACE RP 0487 – Selection and evaluation criteria for petroleum-based intermediate coatings
57 NACE RP 0490 – Detection of defects in fusion-bonded epoxy coatings on pipelines with defect sizes ranging from 250 to 760 micrometers (10–30 mils)
58 NACE RP 0491 – Checklist for selecting non-metallic welding systems for oilfield applications
59 NACE RP 0492 – Metallurgical parameters and inspection requirements for bracelet-type anodes used on submarine pipelines
60 NACE RP 0495 – Guidelines for improving the qualifications of personnel engaged in sandblasting, coating, and lining work in the railway industry
61 NACE RP 0572 – Design, installation, operation, and maintenance of deep-buried impressed current grounding beds
62 NACE RP 0575 – Internal cathodic protection systems for petroleum processing vessels
63 NACE RP 0590 – Recommended methods for detecting, protecting, and repairing cracks in air separators
64 NACE RP 0591 – Coatings for concrete surfaces exposed to non-submerged and atmospheric environments
65 NACE RP 0592 – Application of internal coating systems to new and existing rail tank cars transporting concentrated sulfuric acid (90%–98%)
66 NACE RP 0675 – Corrosion control for external surfaces of submarine steel pipes
67 NACE RP 0690 – Standard format for data collection and editing for input into databases of corrosion-resistant materials
68 NACE RP 0692 – Application of external coating systems to steel railway tank cars
69 NACE RP 0775 – Preparation, installation, and analysis of corrosion coupons in oilfield operations
70 NACE RP 0792 – Standard format for periodic computer-based data surveys
71 NACE RP 0892 – Linings for submerged concrete equipment surfaces
72 NACE TM 0169 – Laboratory corrosion testing of metals
73 NACE TM 0171 – Autoclave corrosion testing of metals in high-temperature water
74 NACE TM 0172 – Determination of corrosion behavior of various materials in petroleum production pipelines
75 NACE TM 0173 – Test method for evaluating the quality of subsurface injection water using membrane filters
76 NACE TM 0174 – Laboratory evaluation methods for protective coatings and lining materials used in equipment containing solutions
77 NACE TM 0177 – Laboratory test methods for metals exhibiting specific forms of cracking under H₂S-containing environments
78 NACE TM 0183 – Evaluation of internally plastic-coated tubular equipment for corrosion control in aqueous flowing media
79 NACE TM 0184 – Accelerated test methods for selecting atmospheric corrosion-resistant surface coatings for offshore platforms and equipment
80 NACE TM 0185 – Autoclave test evaluation of internally corrosion-resistant plastic coatings on tubular equipment
81 NACE TM 0186 – Detection of defects in internal pipe coatings with dry film thicknesses ranging from 250 to 760 micrometers (10–30 mils)
82 NACE TM 0187 – Evaluation of elastomeric materials in sour gas environments
83 NACE TM 0190 – Impressed current test method for laboratory testing of aluminum anodes
84 NACE TM 0192 – Evaluation of elastomeric materials in carbon dioxide compressor environments
85 NACE TM 0193 – Laboratory corrosion testing of metals in refined chemical cleaning solutions at temperatures below 93°C (200°F)
86 NACE TM 0194 – Field monitoring of bacterial growth in oilfield systems
87 NACE TM 0196 – Periodic evaluation of corrosion resistance of polymeric materials
88 NACE TM 0274 – Dynamic corrosion testing of metals in high-temperature water
89 NACE TM 0275 – Testing of steel and fiber-reinforced plastic piston performance using hybrid mixing and alternating rod methods
90 NACE TM 0284 – Evaluation of resistance to hydrogen-induced cracking in pipelines and pressure vessels
91 NACE TM 0286 – Cooling water test apparatus for heat transfer surfaces
92 NACE TM 0294 – Testing of embeddable anodes in atmospherically exposed reinforced concrete
93 NACE TM 0296 – Evaluation of elastomeric materials in acidic liquid environments
94 NACE TM 0374 – Laboratory screening tests for anti-scaling capabilities aimed at preventing calcium sulfate and calcium carbonate deposition
95 NACE TM 0384 – Defect detection in internal pipe coatings with dry film thicknesses less than 250 micrometers (10 mils)