Is further solution treatment required for austenitic stainless steel heads after shape correction?

2015-07-28View Original

Thread Content

I would like to ask: For austenitic stainless steel heads that have been formed by cold working, a solution treatment was carried out after shaping, and deformation occurred. Is it necessary to perform another solution treatment after reshaping? Are there any standards or manuals that cover this section? Thank you!

Reply #22015-07-29

It should not be necessary; generally, the deformation rate of the regular shape is not high. If the deformation rate is greater than 15%, a further solution treatment is required

Reply #32015-07-30

Got it, thanks :victory:

Submit a Project

**Looking for Chemical Technology, Equipment & Solutions?** No Registration Required Broader Platform Exposure | Global Chemical Service Provider Connections

Submit Request — Free Consultation

Disclaimer

This is an automated machine translation of the original thread. Some technical terms may have inaccuracies; the original text shall prevail. Click "View Original" at the top right to access the source page, which supports IP-based automatic real-time language translation. Please watch out for contact details and sales inducements to prevent fraud. All content and translations are for reference only, representing solely the poster's personal views. For enquiries, email service@hcbbs.com.

Is further solution treatment required for austenitic stainless steel heads after shape correction?

Thread Content

Related Threads in This Forum

← Previous

Next →

Submit a Project

Disclaimer

Quick Links