High-temperature and corrosion-resistant reactor
Thread Content
A reactor for the reaction between sulfuric an and fly ash; equipment requirements: mixing rate of 600 kg/h, reaction pressure of 2.0 Mpa, reaction temperature of 320°–350°； Mole ratio: 8:1. Reaction condition: At 213°C, sulfuric acid begins to decompose ammonium bisulfate and ammonia; above 280°C, ammonium bisulfate in molten state reacts with fly ash, and the reaction is more complete above 320°C. The product after the reaction is in the form of a molten liquid ； Please discuss the types of reactors and corrosion-resistant materials ；
I haven’t been involved in this type of production, so I’m just offering some preliminary thoughts. Dried materials are likely not corrosive, and ordinary carbon steel should suffice as the material. Should a boiling furnace be used for the reactor?