Special requirements for duplex stainless steel

Thread Content

Specifications for duplex stainless steel materials – Special requirements 1, Materials 1.1, UNS S31803/S32205 Requirements 1.1.1, All materials shall be subjected to solution annealing and water quenching. 1.1.2 The nitrogen content of all materials should be above 0.14%. 1.1.3 Seamless steel pipes are made from conventional billets. 1.2, UNS S32550 requires 1.2.1: All materials with a thickness of less than 9.5 millimeters (0.375 inches) shall be solution-annealed and then quickly cooled in air or quenched in water. All materials with a thickness of 9.5 millimeters (0.375 inches) or more shall be solution-annealed and quenched in water. 1.2.2 The nitrogen content of all materials shall be above 0.18%. 1.2.3 Seamless steel pipes are made from conventional billets. Seamless steel pipes are made using conventional billet or powder metallurgy methods. 1.3. UNS S32750 requires that 1.3.1, all materials shall be solution annealed and water quenched. 1.3.2 Seamless steel pipes are made from conventional billets. 1.4 The thin steel sheets should be bright-annealed or pickled, with a surface finish of 2D. 1.5 The steel plates should be pickled. 1.6 For steel plates/sheet metals with a thickness of 19 mm (0.75 inches) or less, shearing, wet grinding saw cutting, or plasma arc cutting (PAC) shall be used to achieve the required final width and length. If using PAC, the highest cutting speed should be employed to minimize heat input as much as possible. The cutting angle should not exceed 3 degrees, and the roundness of the top edge at any point along the cut should not exceed 0.8 millimeters (1/32 inch) in radius. The slag on the cut area/adjacent steel plate should be removed to ensure a smooth and uniform final cut surface. 1.7 Processed products obtained through hot forming or cold forming that achieve an external fiber elongation of more than 10% (i.e., end caps, pipe fittings, etc.) shall undergo solution annealing at the temperature specified in the standards, followed immediately by water quenching. Products that have undergone annealing and quenching shall be tested in accordance with 2.1.1, and the test results shall meet the requirements of 3.1.1.1 and 3.1.1.2. 1.7.1 If heat treatment is required during the prefabrication of the head, the temperature should be maintained for at least 30 minutes. The temperature should be recorded using a thermocouple installed on the head. 1.7.2 For products that have been solution-annealed and water-quenched in accordance with the requirements of 1.1.6, the required tests can be carried out using specimens. The samples should be taken from the materials used in the product, as well as from the materials that are processed and annealed/quenched using the product. 1.7.3. In any case, the manufacturing process of the supplier for the processed units must include annealing, quenching, and testing as required by 1.1.6. The supplier shall promptly arrange for the owner’s inspectors to be present on site to witness the supplier’s processing, solution annealing, and quenching. 1.8 The interior and exterior of the processed head shall be inspected by means of coloring. Refer to the acceptance criteria in ASME Chapter VIII, Section 1, Appendix 8. 1.9 The processing unit must purchase materials from qualified suppliers. 2. Test 2.1: According to ASTM A-923 Method C, a corrosion test was conducted to verify the absence of harmful intermetallic phases. Method A of ASTMA-923 should not be used as a basis for accepting materials. 2.1.1 Unless otherwise specified by the Owner, corrosion tests shall be conducted on the following: 2.1.1.1 Steel plates or thin steel plate coils from each heat. 2.1.1.2 Each lot of steel pipes defined in Paragraph 8.1 of ASTM A790. 2.1.1.3 Each lot of steel pipes defined in Note 2, Paragraph 8.3 of ASTM A789. 2.1.1.4 Flanges, castings, and fittings from each heat in each batch of heat treatment. 2.1.1.5 Heat treatment for each batch of other finished products in 1.7. 2.1.2 The test specimens of welded products shall contain the base metal, heat-affected zone, and weld metal. 2.1.3 For materials not listed in Table A-923-3, the test temperatures and acceptance criteria are as follows: for material S32550 (non-welded products), the maximum allowable corrosion rate at the test temperature is 30°C with a standard of 10MDD; for S32550 (welded products), it is 27°C with a standard of 10MDD; for S32750 (welded products), it is 37°C with a standard of 10MDD. 3. Documentation Records 3.1 All materials must be accompanied by a factory inspection report or certificate, confirming that they meet the requirements of these specifications. 3.1.1 All certificates shall report the corrosion rate determined according to 2.1, testing harmful intermetallic phases. The test results should be traceable to the purchased materials. 3.1.2 If required, the applicable certificate shall report the results of the Charpy impact test per ASTM A370. The test results should be traceable to the purchased materials. 4. Welding
4.1. All welding procedure specifications must be verified through corrosion tests; in accordance with ASTM A-923 Method C, they shall contain no harmful intermetallic phases. ASTM A-923 Method A shall not be used as a basis for procedural acceptance. Each program eligibility record requires one test. The test temperature and acceptance criteria shall be the same as the applicable criteria given in 2.1.3 or Table 3 of ASTM A-923. For procedure qualification involving the joining of different duplex stainless steel grades, the test temperature shall be that of the lower test temperature grade.