Does anyone have the parameters regarding the corrosivity of concentrated sulfuric acid? Does the corrosivity change as the concentration varies between 93 and 98?
Concentration is one factor; please also provide the temperature. Additionally, it would be helpful if you could also provide information on which metal materials are available, to facilitate assistance. I remember there was a comprehensive summary article about sulfuric acid on the forum; you might want to take a look first
The concentration is known; now we need the temperature as well. Additionally, it’s important to know under what operating conditions it will be used, such as for transporting acid, returning acid, or feeding acid, etc