Thread Content
-For 35-degree chilled brine, a stop valve is required; PN16 will suffice. I would like to ask if there are any requirements regarding the material used for this valve? The design institute specified CF8; will carbon steel suffice? What model is needed for carbon steel? Thank you all{:3_60:}
Carbon steel will do; chloride ions corrode stainless steel
Oh, okay, thank you. Will ordinary carbon steel be sufficient?
The temperature is too low; is carbon steel suitable?
If carbon steel valves are to be used, it is recommended to choose LCB with J41W-16 material
I’m worried about this too. There’s definitely no problem in the short term, but will LCB material be much more expensive than WCB?