High-temperature temper embrittlement in hydrogenation reactors
Thread Content
Hydrogenation reactors are susceptible to high-temperature temper embrittlement; should a minimum pressure increase temperature be set during operation? If a minimum heating temperature is set, what should that temperature be for SA387GR22CL2? Is it proposed by the design institute or by the manufacturing factory?
25-30° per hour. It should be proposed by the designer
Thank you for the reply! Could you explain in detail how the voltage is increased? At what voltage level does the voltage start to rise? Is there a relationship between voltage rise and temperature?