Issues to consider regarding heat insulation on the surface of stainless steel equipment

Thread Content

Issues to be considered regarding heat insulation on the surface of stainless steel equipment: I. Corrosion and protection of the metal surface. Generally, when applying insulating layers to metal surfaces, not enough attention is paid to the issue of corrosion. In some cases, no measures are taken to protect the metal surface from corrosion during heat insulation work; as a result, corrosion and perforations occur after a few years of use, thereby reducing the equipment’s service life.       1. Analysis of corrosion causes When polyurethane foam plastic is used for insulation. It is primarily an organosynthetic material that is foamed on-site using polyethers and polyisocyanate esters along with various additives and flame retardants. Since the insulation material is dry when in contact with the metal surface during initial use, it does not corrode the metal surface. However, over time, due to temperature differences, moisture inevitably forms between the insulation layer and the metal surface. This has been proven in practical use. Due to the presence of water in the interface layer between polyurethane and metal, the polyurethane material releases substances in the presence of this water, resulting in acidic water with a pH of 3–5. At the same time, it still contains harmful components such as certain chlorides, potassium oxide, and sodium oxide in water. When these insulating materials come into contact with metal surfaces, corrosion occurs, and the reasons for this are as follows: The insulation materials contain water-absorbing substances such as K2O and Na2O, which undergo chemical reactions with moisture. The presence of soluble salts also enhances the condensation of water in the insulating material. Furthermore, under the action of acidic aqueous solutions, the dissolution of soluble substances transforms the water film into a strong electrolyte solution, creating the necessary conditions for the electrochemical corrosion of metals. Therefore, not only carbon steel is prone to corrosion, but stainless steel as well. The main characteristic of corrosion in stainless steel is pitting corrosion as its primary feature.           Therefore, the corrosion resistance of stainless steel surfaces should be considered before insulation is applied.         2. Recommended protective methods: For such corrosion issues, epoxy coatings can be used as a solution. It is important to note that before applying the topcoat, a phosphating primer must be applied to the stainless steel surface first. Since the surface of stainless steel belongs to non-ferrous metals, its oxide film is relatively dense. Generally, the primer of anti-corrosion coatings does not provide good adhesion to non-ferrous metals. Therefore, a layer of interface agent must be applied to improve the adhesion between the primer and the metal surface. The main function of a phosphating primer is to allow phosphoric acid to react with the metal surface to form a passivating film of new phosphates. The function of this membrane is to become one with the metal, forming chemical bonds. It also has excellent adhesion to non-metallic coatings.      Additionally, a primer with good adhesion to non-ferrous metals can be considered. II. Regarding moisture prevention outside the insulation layer: Due to the temperature difference effects that occur during the operation of insulation equipment and pipelines. In other words, moisture often accumulates on the outer surface of the insulation layer, which in turn has a corrosive effect on the protective layer used. Therefore, it is common practice to apply 5 millimeters of asphalt mastic on the surface of the insulation layer as a moisture barrier.