For temperature sensing in exhaust systems, the protective sleeves corrode and become punctured after some time; what material would be suitable for use? It turned out that 316 was used
What are the components of exhaust gas? You can try lining it with plastic
The medium temperature and pressure need to be specified. If it is highly corrosive, the casing can be lined with plastic.
How to choose without information on exhaust components, temperature, and pressure? HC type, tantalum sleeves, enamel with tantalum studs, fluorinated lining, etc
It can be lined with PTFE; I produce it, so feel free to contact me if you need it
It depends on the specific circumstances: whether to choose PTFE lining or a material with better corrosion resistance
The operating conditions must be specified, including the medium composition, temperature, flow rate, etc. If the temperature is low, a temperature- and corrosion-resistant material can be used as lining inside the protective sleeve. If it is a high-temperature environment, it is necessary to choose metals, alloy steels, ceramics, or similar materials that can withstand such media.