How to form S25073 duplex steel heads?

2015-06-21View Original

Thread Content

I would like to ask everyone: How is it possible to shape S25073 duplex steel headings? What is the general process?

Reply #22015-06-23

The head factory performs direct spinning and cold forming.

Reply #32015-06-23

Double-phase stainless steel end caps can be formed by spinning or cold stamping. After formation, they must undergo solution treatment, and measures to prevent deformation should also be taken during this process. There are specialized manufacturers that produce such shaped end caps.

Reply #42015-06-24

Since solution treatment is still required after stamping, why not use hot pressing? Can’t we carry out solution treatment after hot pressing?

Submit a Project

**Looking for Chemical Technology, Equipment & Solutions?** No Registration Required Broader Platform Exposure | Global Chemical Service Provider Connections

Submit Request — Free Consultation

Disclaimer

This is an automated machine translation of the original thread. Some technical terms may have inaccuracies; the original text shall prevail. Click "View Original" at the top right to access the source page, which supports IP-based automatic real-time language translation. Please watch out for contact details and sales inducements to prevent fraud. All content and translations are for reference only, representing solely the poster's personal views. For enquiries, email service@hcbbs.com.

How to form S25073 duplex steel heads?

Thread Content

Related Threads in This Forum

← Previous

Next →

Submit a Project

Disclaimer

Quick Links